Copper Foil for Battery Anode Substrate (9um thick)
-
Price:
Negotiable
- minimum:
- Total supply:
-
Delivery term:
The date of payment from buyers deliver within days
-
seat:
Shandong
-
Validity to:
Long-term effective
-
Last update:
2017-12-01 01:46
-
Browse the number:
250
+
- Contactaixin:
Ms. Amy(Mr.)
- Email: telephone:
-
Arrea:
Shandong
Address:No. 2728 Golden Plaza, Yimeng Road, Lanshan District Linyi, Shandong, China
- Website:
+
This copper foil (9 um ) is used as a substrate for coating anode materials in Li-Ion battery research.
Specifications
- Material: Copper, Purity> 99.99%
- One side: Polished
- One side: Matt
-
Sold in roll onlyShipped in vacuum bag
- Length: 190m
- Width: 280mm
- Thickness: 9 um
- Density: 8.94 g·cm−3
- Net weight: 5.5 kg
- Tube weight: 1 kg
Packaging & Shipping
1 Standard exported package: Internal anticollision protection, external export wooden box packaging.
2 Shipping by Fedex, by air, by sea according to customers' requirements to find the most suitable way,
3 Responsible for the damage during the shipping process, will change the damage part for you for free.
4 within 7 workdays after order confirmed
4.Related:
Coating machine for Aluminum Foil and Copper Foil :
1. Automatic Roll to Roll Battery Electrode Coating System (Max. 250mm Width) with Drying Oven -AFA-E300 :
2. Compact Tape Casting Film Coater with Dryer, Vacuum Chuck & Adjustable Film Applicator (110 or 220VAC) - GN-AFA-III :
Item |
nominal thickness |
|||||||||
Double shiny |
Single (double) matte |
Super matte |
||||||||
8µm |
9µm |
12µm |
15µm |
20µm |
10µm |
12µm |
10µm |
12µm |
||
Area Weight (g/m2) |
70~75 |
85~90 |
100~105 |
128~133 |
175~181 |
95~100 |
105~110 |
95~100 |
105~110 |
|
Tensile Strength (kg/mm2) |
Normal temperature |
≥30.0 |
≥30.0 |
≥30.0 |
≥30.0 |
≥30.0 |
≥25.0 |
≥25.0 |
≥25.0 |
≥25.0 |
Elongation (%) |
Normal temperature |
≥5.0 |
≥5.0 |
≥5.0 |
≥6.0 |
≥8.0 |
≥2.5 |
≥2.5 |
≥3.0 |
≥3.0 |
Roughness Rz(µm) |
≤3.0 |
negotiable |
||||||||
Thickness (µm) |
(-0;+3) |
negotiable |
||||||||
Oxidation resistance (160°C/10min) |
No oxidation and discoloration |